Modification of NR/EPDM/Carbon Black Composites by Co-vulcanization using High Energy -radiation: Effect of Sensitizer Concentration
S. Siriwardena - ไม่ระบุหน่วยงาน
ชื่อเรื่อง (EN): Modification of NR/EPDM/Carbon Black Composites by Co-vulcanization using High Energy -radiation: Effect of Sensitizer Concentration
ผู้แต่ง / หัวหน้าโครงการ (EN): S. Siriwardena
บทคัดย่อ (EN): The effect of sensitizer concentration on the mechanical properties of irradiated NR/EPDM/CB (70/30/30) composites was studied. Polyethylene glycol 400 diacrylate (A-400) was used as the sensitizer and its concentration was varied from 0 to 8 phr. The composites were irradiated at 80 and 100 kGy irradiation doses. Non-sensitized composites irradiated at 100 kGy exhibited better mechanical properties than that of irradiated at 80 kGy except for elongation at break (Eb). However, the composites irradiated at 80 kGy in the presence of the sensitizer showed higher tensile strength and Eb, lower abrasion weight loss and tear strength. Neither irradiation dose nor sensitizer concentration has shown a significant effect on the modulus and hardness of the composites. The addition of a sensitizer resulted in improvement of mechanical properties except the modulus, until sensitizer level reached an optimum concentration beyond which properties dropped gradually. The optimum concentration of sensitizer to obtain the best mechanical properties of the composites irradiated both at 80 and 100 kGy was found to be 1 phr. Therefore, this concentration of polyethylene glycol 400 diacrylate was considered the best for sensitizing NR/EPDM/CB composites.
บทคัดย่อ: ไม่พบข้อมูลจากหน่วยงานต้นทาง
ภาษา (EN): en
เผยแพร่โดย (EN): การยางแห่งประเทศไทย
คำสำคัญ (EN): NR/EPDM
เจ้าของลิขสิทธิ์ (EN): การยางแห่งประเทศไทย
หากไม่พบเอกสารฉบับเต็ม (Full Text) โปรดติดต่อหน่วยงานเจ้าของข้อมูล

การอ้างอิง

S. Siriwardena. "Modification of NR/EPDM/Carbon Black Composites by Co-vulcanization using High Energy -radiation: Effect of Sensitizer Concentration". ไม่ระบุหน่วยงาน. ม.ป.ป.

S. Siriwardena. "Modification of NR/EPDM/Carbon Black Composites by Co-vulcanization using High Energy -radiation: Effect of Sensitizer Concentration". ไม่ระบุหน่วยงาน. ม.ป.ป.. Print.



TARR Wordcloud:
Modification of NR/EPDM/Carbon Black Composites by Co-vulcanization using High Energy -radiation: Effect of Sensitizer Concentration
S. Siriwardena
การยางแห่งประเทศไทย
ไม่ระบุวันที่เผยแพร่
Effect of Carbon Black and BaSo4 on the Thermo-Chemical Resistance of Natural Rubber Composite THE EFFECTS OF CARBON BLACK ON PROPERTIES OF RICE HUSK ASH FILLED HYBRID NATURAL RUBBER COMPOSITES CARBON, WATER AND ENERGY BALANCE OF RUBBER ECOSYSTEM Effect of cholesterol loaded cyclodextrin on cryosurvivability of buffalo spermatozoa (Buffalo Bulletin,40(1)) Carcinogenic potential of high aspect ratio carbon nanomaterials A METHOD FOR PRODUCING CARBON BLACK SILICA MASTER BATCH Gibbs energy additivity approaches to QSPR in modeling of high pressure density and kinematic viscosity of FAME and biodiesel Estimation of biomass and carbon stock in Para rubber plantations using object-based classification from Thaichote satellite data in Eastern Thailand Use of Coconut Pith as Bio Filler for EPDM Rubber Composites The source of latex. Tracing carbon from leaf photosynthesis to latex metabolism in rubber trees using carbon stable isotopes
คัดลอก URL
กระทู้ของฉัน
ผลการสืบค้นทั้งหมด โพสต์     เรียงลำดับจาก
พัฒนาระบบโดยศูนย์ความรู้เฉพาะด้านวิศวกรรมความรู้และวิศวกรรมภาษาDeveloped by Center of Excellence for Unified Knowledge and Language Engineering
สนับสนุนโดยสำนักงานพัฒนาการวิจัยการเกษตร (องค์การมหาชน)Supported by the Agricultural Research Development Agency (Public Organization)
แบบสำรวจความพึงพอใจQuestionair