การแคลซิเนชันยิปซัมที่เป็นผลิตภัณฑ์รองจากกระบวนการทางเคมี
สุธารี เกียรติมั่นง - มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี
ชื่อเรื่อง: การแคลซิเนชันยิปซัมที่เป็นผลิตภัณฑ์รองจากกระบวนการทางเคมี
ชื่อเรื่อง (EN): Calcination of Byproduct Gypsum
ผู้แต่ง / หัวหน้าโครงการ: สุธารี เกียรติมั่นง
บทคัดย่อ (EN): This research aimed to verify the Through Solution Mechanism proposedpreviously by Vorapruckjaru and study the effect of salt ion for better understandingthe wet process dehydration of byproduct gypsum.The a-hemihydrate calcium sulfate was prepared by using byproductgypsum from Thai Union Paper Co., Ltd. as raw material. The investigation of theeffect of salt solution was performed by dehydrating the byproduct gypsum in 2SM,3M, 4M, of calcium chloride solution. It was concluded from the results that thedehydration rate increased rapidly when the dehydration process was performed inhigh concentration of calcium chloride solution. Nevertheless, the dehydrationprocess in high concentration of calcium chloride solution produced small crystal ofa-hemihydrate calcium sulfate. The Through Solution Mechanism could bedescribed by the results of dehydration process observation. This mechanism wasdivided into three stages. The first stage was the dissolution of gypsum in solution.Thegypsum or dihydrate calcium sulfate was dissolved then the solution wassaturated with the gypsum. Thls stage depended on the solubility of gypsum incalcium chloride solution. Right after the gypsum reached the saturation point, thecrystals of a-hemihydrate calcium sulfate were formed immediately in the secondstage. In the final stage, the dehydration process nearly completed. From the resultsof dehydration process observation, the function of CaC12 in the process could beproposed. The first function is the accelerating the dehydration process to reachsaturated situation. For the second function, calcium and chloride ions attractedwater molecules in order to withhold the water bonding in crystalline structure ofhemihydrate calcium sulfate. The third function, calcium and chloride ionsprevented the agglomeration of hemihydrate calcium sulfate crystals. However, thecrystallization of hemihydrate calcium sulfate would be inhibited if the amounts ofions were too high. The hemihydrate calcium sulfate crystal obtained fromdehydration of byproduct gypsum was transparent rod shape. The smallerhemihydrate calcium sulfate crystal obtained fiom the high concentration (4M) ofcalcium chloride solution results in the low quality of a-hemihydrate calcium sulfate(i.e. high normal consistency, long setting time, low compressive strength).However, the hemihydrate calcium sulfate crystal obtained in this research gave poorphysical properties when prepared as plaster. Thus, byproduct gypsum obtainedfiom paper manufacturing did not appropriate for preparing the x-hemihydratecalcium sulfate using wet process.
บทคัดย่อ: ไม่พบข้อมูลจากหน่วยงานต้นทาง
ภาษา (EN): th
เอกสารแนบ: http://dcms.thailis.or.th/dcms/dccheck.php?Int_code=54&RecId=5900&obj_id=17086
เผยแพร่โดย: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี
คำสำคัญ (EN): Wet Process Dehydration of GypsurnlByproduct Gypsum
เจ้าของลิขสิทธิ์: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี
รายละเอียด: This research aimed to verify the Through Solution Mechanism proposedpreviously by Vorapruckjaru and study the effect of salt ion for better understandingthe wet process dehydration of byproduct gypsum.The a-hemihydrate calcium sulfate was prepared by using byproductgypsum from Thai Union Paper Co., Ltd. as raw material. The investigation of theeffect of salt solution was performed by dehydrating the byproduct gypsum in 2SM,3M, 4M, of calcium chloride solution. It was concluded from the results that thedehydration rate increased rapidly when the dehydration process was performed inhigh concentration of calcium chloride solution. Nevertheless, the dehydrationprocess in high concentration of calcium chloride solution produced small crystal ofa-hemihydrate calcium sulfate. The Through Solution Mechanism could bedescribed by the results of dehydration process observation. This mechanism wasdivided into three stages. The first stage was the dissolution of gypsum in solution.Thegypsum or dihydrate calcium sulfate was dissolved then the solution wassaturated with the gypsum. Thls stage depended on the solubility of gypsum incalcium chloride solution. Right after the gypsum reached the saturation point, thecrystals of a-hemihydrate calcium sulfate were formed immediately in the secondstage. In the final stage, the dehydration process nearly completed. From the resultsof dehydration process observation, the function of CaC12 in the process could beproposed. The first function is the accelerating the dehydration process to reachsaturated situation. For the second function, calcium and chloride ions attractedwater molecules in order to withhold the water bonding in crystalline structure ofhemihydrate calcium sulfate. The third function, calcium and chloride ionsprevented the agglomeration of hemihydrate calcium sulfate crystals. However, thecrystallization of hemihydrate calcium sulfate would be inhibited if the amounts ofions were too high. The hemihydrate calcium sulfate crystal obtained fromdehydration of byproduct gypsum was transparent rod shape. The smallerhemihydrate calcium sulfate crystal obtained fiom the high concentration (4M) ofcalcium chloride solution results in the low quality of a-hemihydrate calcium sulfate(i.e. high normal consistency, long setting time, low compressive strength).However, the hemihydrate calcium sulfate crystal obtained in this research gave poorphysical properties when prepared as plaster. Thus, byproduct gypsum obtainedfiom paper manufacturing did not appropriate for preparing the x-hemihydratecalcium sulfate using wet process.
หากไม่พบเอกสารฉบับเต็ม (Full Text) โปรดติดต่อหน่วยงานเจ้าของข้อมูล

การอ้างอิง

สุธารี เกียรติมั่นง. "การแคลซิเนชันยิปซัมที่เป็นผลิตภัณฑ์รองจากกระบวนการทางเคมีCalcination of Byproduct Gypsum". มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. 2544

สุธารี เกียรติมั่นง. "การแคลซิเนชันยิปซัมที่เป็นผลิตภัณฑ์รองจากกระบวนการทางเคมีCalcination of Byproduct Gypsum". มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. 2544. Print.



TARR Wordcloud:
การแคลซิเนชันยิปซัมที่เป็นผลิตภัณฑ์รองจากกระบวนการทางเคมี
สุธารี เกียรติมั่นง
มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี
2544
การลดจำนวนผลิตภัณฑ์ที่บกพร่องในกระบวนการเคลือบแบบหลายแผ่นด้วยวิธีการซิกซ์ซิกม่า การศึกษาผลของกระบวนการผลิตและการเก็บรักษาต่อปริมาณสารพฤกษเคมีและฤทธิ์การต้านอนุมูลอิสระในผลิตภัณฑ์เคร การลดผลิตภัณฑ์ที่มีข้อบกพร่องในกระบวนการผลิตเมมเบรนสวิตช์ โดยการประยุกต์ใช้แนวทางซิกส์ ซิกมา การลดจำนวนผลิตภัณฑ์บกพร่องจากการบรรจุในกระบวนการผลิตชิ้นส่วนรถยนต์ การเก็บเกี่ยวสาหร่ายขนาดเล็กในการเพาะเลี้ยงแบบน้ำเขียวด้วยกระบวนการรวมตัวและตกตะกอนทางเคมี การบำบัดน้ำเสียจากโรงงานผลิตสี โดยกระบวนการตกตะกอนทางเคมี การวิเคราะห์การใช้สารเคมีในกระบวนการผลิตลำไยโดยเทคนิคการประมวลผลภาพ การลดจำนวนของเสียที่เกิดจากการบวมของผลิตภัณฑ์วุ้นมะพร้าวในกระบวนการบรรจุ ศักยภาพของชุมชนด้านผลิตภัณฑ์ โครงการ "หนึ่งตำบล หนึ่งผลิตภัณฑ์" อำเภอเมือง จังหวัดจันทบุรี การลดปริมาณผลิตภัณฑ์บกพร่องในกระบวนการหล่อขึ้นรูปของมิเตอร์น้ำ GMK 15
คัดลอก URL
กระทู้ของฉัน
ผลการสืบค้นทั้งหมด โพสต์     เรียงลำดับจาก
พัฒนาระบบโดยศูนย์ความรู้เฉพาะด้านวิศวกรรมความรู้และวิศวกรรมภาษาDeveloped by Center of Excellence for Unified Knowledge and Language Engineering
สนับสนุนโดยสำนักงานพัฒนาการวิจัยการเกษตร (องค์การมหาชน)Supported by the Agricultural Research Development Agency (Public Organization)
แบบสำรวจความพึงพอใจQuestionair