การพัฒนาออกแบบเม็ดดูดซับเซรามิคผลิตจากกากกาแฟ
ไชยยันต์ ไชยยะ - มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี
ชื่อเรื่อง: การพัฒนาออกแบบเม็ดดูดซับเซรามิคผลิตจากกากกาแฟ
ผู้แต่ง / หัวหน้าโครงการ: ไชยยันต์ ไชยยะ
บทคัดย่อ (EN): The objectives of this work were to study factors affecting the forming of made the adsorbent comprised of coffee residue and clay, to investigate the capacity of heavy metal ions adsorption, to elucidate adsorption mechanism of adsorbent by varying pH and temperature, to coniirm the adsorption efiiciency of the adsorbent after regenerated with water and to compare the adsorption performance between the adsorbent and activated carbon. Firstly, we studied the factors of temperature, the weight ratios between coffee residue and clay and the diameter affecting the formation of the adsorbent. The experimental results demonstrated that the weight ratio of coffee residue to clay of 80:20, the diameter of 4 rnrn. and 0 the pyrolysis temperature 500 C for 2 hours were the suitable forming condition of the adsorbent. The adsorption reached equilibrium in 30 min. and followed the Langmuir adsorption isotherm. The maximum adsorption capacity (V) of the adsorbent for several heavy metal ions of Cd, Cu, Pb, Zn and Ni as high as 39.52, 31.15, 19.53, 13.39 and 11.0 mg-metal/g-adsorbent respectively. In the study of mechanism, the maximum adsorption capacity (Vm) decreased with the decreasing pH and increased with the increasing the solution temperature. The heat of adsorption (AH ) was calculated to be 1.1 1 kcal./mol demonstrated that the adsorption should be the physical adsorption. In the regeneration experiments, the adsorbed ions were almost (90%) removed by rinsing with water and the adsorption capacity decreased slightly (10%) after three times regeneration. In addition, with the analytical results of FT-IR and Zeta potential meter, we found that there were functional groups of 0-H, C=O and C-N groups on the adsorbent surfaces which have the electrical charge of -37.1 mV. It may be concluded that the adsorption was controlled by electrostatic force between 0-H, C=O and C-N functional groups charged with negative electric charges and the positive charged heavy metal ions. In the adsorption performance comparison between the adsorbent and activated carbons, bough the maximum adsorption capacity per weight of activated carbon was larger than which of the adsorbent, however the maximum adsorption capacity per specific area was smaller, since the adsorption characteristic of the adsorbent was controlled by electrostatic force.
บทคัดย่อ: ไม่พบข้อมูลจากหน่วยงานต้นทาง
ภาษา (EN): th
เอกสารแนบ: http://dcms.thailis.or.th/dcms/dccheck.php?Int_code=54&RecId=6191&obj_id=17948
เผยแพร่โดย: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี
คำสำคัญ (EN): Zeta Potential
เจ้าของลิขสิทธิ์: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี
รายละเอียด: The objectives of this work were to study factors affecting the forming of made the adsorbent comprised of coffee residue and clay, to investigate the capacity of heavy metal ions adsorption, to elucidate adsorption mechanism of adsorbent by varying pH and temperature, to coniirm the adsorption efiiciency of the adsorbent after regenerated with water and to compare the adsorption performance between the adsorbent and activated carbon. Firstly, we studied the factors of temperature, the weight ratios between coffee residue and clay and the diameter affecting the formation of the adsorbent. The experimental results demonstrated that the weight ratio of coffee residue to clay of 80:20, the diameter of 4 rnrn. and 0 the pyrolysis temperature 500 C for 2 hours were the suitable forming condition of the adsorbent. The adsorption reached equilibrium in 30 min. and followed the Langmuir adsorption isotherm. The maximum adsorption capacity (V) of the adsorbent for several heavy metal ions of Cd, Cu, Pb, Zn and Ni as high as 39.52, 31.15, 19.53, 13.39 and 11.0 mg-metal/g-adsorbent respectively. In the study of mechanism, the maximum adsorption capacity (Vm) decreased with the decreasing pH and increased with the increasing the solution temperature. The heat of adsorption (AH ) was calculated to be 1.1 1 kcal./mol demonstrated that the adsorption should be the physical adsorption. In the regeneration experiments, the adsorbed ions were almost (90%) removed by rinsing with water and the adsorption capacity decreased slightly (10%) after three times regeneration. In addition, with the analytical results of FT-IR and Zeta potential meter, we found that there were functional groups of 0-H, C=O and C-N groups on the adsorbent surfaces which have the electrical charge of -37.1 mV. It may be concluded that the adsorption was controlled by electrostatic force between 0-H, C=O and C-N functional groups charged with negative electric charges and the positive charged heavy metal ions. In the adsorption performance comparison between the adsorbent and activated carbons, bough the maximum adsorption capacity per weight of activated carbon was larger than which of the adsorbent, however the maximum adsorption capacity per specific area was smaller, since the adsorption characteristic of the adsorbent was controlled by electrostatic force.
หากไม่พบเอกสารฉบับเต็ม (Full Text) โปรดติดต่อหน่วยงานเจ้าของข้อมูล

การอ้างอิง

ไชยยันต์ ไชยยะ. "การพัฒนาออกแบบเม็ดดูดซับเซรามิคผลิตจากกากกาแฟ". มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. 2542

ไชยยันต์ ไชยยะ. "การพัฒนาออกแบบเม็ดดูดซับเซรามิคผลิตจากกากกาแฟ". มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. 2542. Print.



TARR Wordcloud:
การพัฒนาออกแบบเม็ดดูดซับเซรามิคผลิตจากกากกาแฟ
ไชยยันต์ ไชยยะ
มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี
2542
ประสิทธิภาพในการดูดซับโลหะหนักโครเมียมโดยกากกาแฟที่ผ่านการใช้ประโยชน์ ในการผลิตเม็ดสี การศึกษาการสกัดและสมบัติของเซอีนจากกากที่เหลือจากการผลิตนมข้าวโพด การดูดซับแก๊สโพรเพนด้วยตัวดูดซับชนิดถ่านที่เตรียมจากกะลามะพร้าวโดยการกระตุ้นด้วยซิงก์คลอไรด์ เชื้อเพลิงอัดแท่งจากกากกาแฟ การศึกษาเปรียบเทียบประสิทธิภาพการดูดซับน้ำมันของเยื่อกระดาษและตัวดูดซับชนิดโพลีโพรไพลีน การบำบัดน้ำเสียหมึกพิมพ์แฟล็กโซกราฟีฐานน้ำโดยกระบวนการโคแอคกูเลชั่น ร่วมกับการดูดซับด้วยกากโลหะไฮดรอกไซด์ ผลิตภาพของปัจจัยการผลิตโดยรวมของการผลิตอ้อยเพื่อใช้ผลิตเอทานอลใน อำเภอแม่สอด จังหวัดตาก การลดเวลานำในการผลิตและงานระหว่างผลิตในการผลิตตู้นิรภัยโดยใช้เทคนิคการผลิตแบบลีน การพัฒนาและปรับปรุงวัสดุดูดซับราคาถูกเพื่อใช้ในการดูดซับสีย้อมรีแอคทีฟ และสีย้อมเบสิก
คัดลอก URL
กระทู้ของฉัน
ผลการสืบค้นทั้งหมด โพสต์     เรียงลำดับจาก
พัฒนาระบบโดยศูนย์ความรู้เฉพาะด้านวิศวกรรมความรู้และวิศวกรรมภาษาDeveloped by Center of Excellence for Unified Knowledge and Language Engineering
สนับสนุนโดยสำนักงานพัฒนาการวิจัยการเกษตร (องค์การมหาชน)Supported by the Agricultural Research Development Agency (Public Organization)
แบบสำรวจความพึงพอใจQuestionair